尖晶石锂锰氧化物锂离子嵌脱过程的交流阻抗谱研究

用粉末微电极研究了尖晶石锂锰氧化物在不同嵌锂状态下嵌脱锂过程的交流阻 抗图谱，提出了新的等效电路模型。描述锂离子在固体中扩散的Warburg阻抗与累 积或消耗的嵌入电容在Lix MnO4中的x≤0．5时串联，0．5＜x≤1时并联。用提出 的等效电路模型分阶段拟合了实验所得的交流阻抗谱，拟合值与实验值相当吻合， 由拟合结果得到不同电位下锂离子在表面膜中的迁移电阻和电容，界面电荷传递电 阻，双层电容，锂离子在固体中扩散系数和累积或消耗的嵌入电容。     

Effect of BaBiO3 and Ba0.6K0.4BiO3 additives on the rechargeability of manganese oxide cathodes in alkaline cells

The effect of the incorporation of small amounts (1–5 wt%) of semiconducting BaBiO₃ and metallic Ba_0.6K_0.4BiO₃ additives on the rechargeability of electrolytic manganese dioxide (EMD) cathodes in alkaline cells in the one-electron regime has been investigated. Both the BaBiO₃ and Ba_0.6K_0.4BiO₃ additives lead to better cyclability compared to the previously known binary oxide additive Bi₂O₃. X-ray diffraction patterns recorded before and after 30 cycles as well as cyclic voltammograms recorded after first and 30 cycles reveal that the better cyclability in the presence of BaBiO₃ and Ba_0.6K_0.4BiO₃ additives is due to the suppression of the formation of unwanted, electrochemically inactive birnessite and hausmannite phases and a shifting of the second-electron capacity of Mn to higher potentials.     

酯交换法合成碳酸二苯酯用氧化铅－氧化锌催化剂的研究

 制备了一种用于苯酚与碳酸二甲酯酯交换合成碳酸二苯酯的新型氧化铅－氧化锌多相催化剂．研究了制备方法、焙烧温度、不同母体和母体配比对催化剂催化性能的影响．应用XRD，TPR和原子吸收光谱对催化剂结构进行了表征，发现Pb3O4是主活性物相，ZnO为助催化剂，并以非晶态或微晶态存在于催化剂体系中．当焙烧温度为500℃，n（Pb）／n（Zn）≈2时，催化剂的活性最高，碳酸二苯酯产率可达45．6％．考察了催化剂的重复使用效果，并对失活原因进行了探讨．     

甲醇与乙醇一步合成异丁醛用CuO-ZnO/Al2O3催化剂

在ＣｕＯ－ＺｎＯ／Ａｌ２Ｏ３催化剂上，甲醇与乙醇在常压和２１０￣３６０℃温度下一步反应合成异丁醛。利用正交设计方法，研究了ＣｕＯ－ＺｎＯ／Ａｌ２Ｏ３体系催化剂组成和制备条件等因素对催化剂催化性能的影响。结果表明，催化剂中ＣｕＯ含量对催化剂的催化活性影响最大，而ＺｎＯ含量则主要影响催化剂对异丁醛的选择性。催化剂制备条件，如沉淀温度、陈化时间等，也不同程度也影响催化剂的催化性能。ＸＲＤ和ＢＥＴ表征结果     

1,10-双(1′-苯基-3′-甲基-5′-氧代吡唑-4′-基)癸二酮-[1,10]与三苯基氧化膦对钐(Ⅲ)的协同萃取行为研究

研究了１，１０－双（１′－苯基－３′－甲基－５′－氧代吡唑－４－基）癸二酮－［１，１０］（ＢＰＭＰＤＤ，Ｈ２Ａ）与三苯基氧化膦（ＴＰＰＯ，Ｂ）的氯仿溶液从硝酸介质中对Ｓｍ（Ⅲ）的协同萃取行为，计算了体系的酸性协萃系数ＲＡ和协萃系数Ｒ，用斜率法测得协萃合物的组成为ＳｍＡ·ＨＡ·Ｂ，计算了协萃平衡常数，用萃取法制得了固态协萃合物，并对其组成、ＩＲ及ＴＧ－ＤＴＡ进行了研究     

甲苯气相选择性氧化制苯甲醛 Ⅰ．V_2O_5／TiO_2－Al_2O_3催化剂研究

制备了一系列负载型Ｖ－Ｔｉ－Ａｌ－Ｏ催化剂并用于甲苯的气相选择性氧化制苯甲醛，考察了接触时间、氧浓度、Ｖ２Ｏ５负载量以及催化剂焙烧温度对反应性能的影响。用ＴＰＲ、ＸＲＤ和ＢＥＴ等测试手段，对催化剂进行了表征。研究发现，催化剂在７７３Ｋ时活化，接触时间１．２秒，氧浓度２１％时，可获得较好的反应结果，Ｖ２Ｏ５负载量为６（ｗｔ）％的催化剂，在５９３Ｋ时反应，得到了转化率２０．５％，苯甲醛产率８．３％的最好结果。     

Ein Beitrag über Oxide vom Typ AMO4 (A = Ti3+, Cr3+; M = Nb5+, Ta5+)

A Contribution on Ternary Oxides of the AMO₄-Type (A = Ti³⁺, Cr³⁺; M = Nb⁵⁺, Ta⁵⁺ ) CrNbO₄, CrTaO₄, TiNbO₄, and TiTaO₄ were prepared by CO₂-laser technique. X-ray single crystal investigations show a random distribution of the metal ions in Rutil type structure, space group D–P4₂/mnm. Calculations of the free energy of reaction between Ti₂O₃ and Nb₂O₅ show higher stability of TiO₂ beside NbO₂. In TiNbO₄ both metals exhibit the oxidation state +4.     

光谱复杂的稀土基体中稀土杂质ICP光谱测定的一些问题

ICP激发光源以其独特的功能使ICP/AES技术在稀土分析中的应用日益广泛,在一定程度上取代了经典的直流电弧光谱法,但应指出,由于常规雾化器的低雾化效率(≤5％)和试样的高倍稀释,ICP/AES技术的实际检测能力的改善并不明显,本文用ICP光谱法测定了     

碱改性γ－Al_2O_3催化剂表面碱强度分布与COS水解活性的研究

用非水滴定法和Ｈａｍｍｅｔｔ系列指示剂测定了ＣＯＳ水解碱改性γ－Ａｌ_２Ｏ_３催化剂的表面碱强度分布．发现表面碱强度分布不均匀与表面能量分布不均匀相呼应．采用零点酸碱强度（Ｈ_（０，ｍａｘ））及碱中心区域分析法，Ｂｒｏｎｓｔｅｄ催化定律，进一步证实ＣＯＳ水解反应具有明显碱催化特征，较高活性催化剂的Ｈ_（０，ｍａｘ）一般为１０左右，对ＣＯＳ水解反应起主要作用的碱性中心的碱强度（Ｈ_０）为４．８≤Ｈ_０≤９．８．对碱金属氧化物改性后的γ－Ａｌ_２Ｏ_３催化剂，Ｂｒｏｎｓｔｅｄ规律在每个碱强度分区域内是适用的．     

碳酸氢铵沉淀法制备氧化钇粉体时反应条件对产物粒度的影响

研究了碳酸氢铵沉淀法的反应条件对氧化钇粒度的影响,探讨了粒度变化规律。发现在沉淀反应中,晶型碳酸钇铵的形成与否是影响氧化钇粒度的关键因素。在较低的反应温度下,当碳酸氢铵和氯化钇的浓度大于0.25mol·L-1,摩尔比大于5,陈化时间大于60min时得到碳酸钇铵沉淀,经煅烧可获得粒度(D50)大于1μm的氧化钇。当反应物浓度较低、摩尔比小,陈化时间较短时得到无定型碳酸钇沉淀,煅烧沉淀可获得粒度(D50)小于0.5μm的氧化钇。实验证明选择适当的沉淀反应条件,可制备D50在0.3～10μm范围内的不同粒度级别的氧化钇粉体。